Effect of sub-zero treatment on the microstructure and hardness of high-chromium white cast iron
Listed in DataCite
ABSTRACT The effect of the sub-zero treatment temperature on the transformation of retained austenite to martensite in two high chromium white cast irons (ASTM A532 Class II Type B) was studied.
Description
The sub-zero treatment applied to each alloy in the as cast condition was performed at -40, -65 and -180 ° C for 10 minutes; after the holding time was completed the samples were cooled to room temperature. The microstructure of the as cast condition was analyzed by optical microscopy (LOM) and scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) analysis was also performed with the aim to identify the microconstituents initially present in each alloy.
The metallographic characterization of the specimens subjected to sub-zero treatment was performed by optical microscopy. Furthermore, Brinell hardness was measured in the as cast and sub-zero treated samples. The alloys studied have important differences in chemical composition, mainly in the molybdenum and copper content, which mainly determine its microstructure.
Read the rest (1 more)
The results showed an increase in the hardness of both alloys with decreasing treatment temperature; which is due to the fact that the amount of retained austenite transformed to martensite increases as the martensite finish temperature (Mf) is reached. It was also observed that a higher molybdenum content produces a metastable austenitic matrix in the as cast samples. Furthermore, the effect of Mo and other alloying elements substantially stabilizes the austenite, obtaining low amounts of martensite after the sub-zero treatment, even at -180 ° C.
Links
Where it is published
- Repository landing page scielo.figshare.com/articles/Effect_of_sub-zero_treatment_on_the_microstructure_an… ↗
landing page · from DataCite
- DOI doi.org/10.6084/m9.figshare.6857792 ↗
DOI / persistent id · from DataCite
Documentation and papers
- Creative Commons Attribution 4.0 International creativecommons.org/licenses/by/4.0/legalcode ↗
license · from DataCite
- IsSupplementTo 10.1590/s1517-707620180002.0370 doi.org/10.1590/s1517-707620180002.0370 ↗
publication · from DataCite
Catalogue records · 2
- DataCite API api.datacite.org/dois/10.6084/m9.figshare.6857792 ↗
metadata API · from DataCite
- DataCite Commons commons.datacite.org/doi.org/10.6084/m9.figshare.6857792 ↗
catalogue entry · from DataCite
Topics
- Stated by source
- Civil engineering · Materials engineering
- Inferred from text
- Materials engineering 70% · Microscopy 75%
Related
Provenance · 1 source records, 12 field assertions
| Source | Key | Last seen | Raw |
|---|---|---|---|
| DataCite | 10.6084/m9.figshare.6857792 | 13 d ago | JSON v1 |
| Field | Assertion | Extractor | Evidence |
|---|---|---|---|
| access_level | source · DataCite | connector:datacite@1.0.0 | /data/attributes/rightsList |
| byte_size | source · DataCite | connector:datacite@1.0.0 | |
| concepts[field].anzsrc:group:4016 | enrichment · DataCite | taxonomy-embedding@1.0.0 | title+keywords+description (70%) |
| concepts[field].fos:civil-engineering | source · DataCite | connector:datacite@1.0.0 | |
| concepts[field].fos:materials-engineering | source · DataCite | connector:datacite@1.0.0 | |
| concepts[modality].local:modality:microscopy | enrichment · DataCite | keyword-concept-rules@1.0.0 | title+description (75%) |
| created_date | source · DataCite | connector:datacite@1.0.0 | |
| description | source · DataCite | connector:datacite@1.0.0 | /data/attributes/descriptions |
| license | source · DataCite | connector:datacite@1.0.0 | /data/attributes/rightsList |
| publication_date | source · DataCite | connector:datacite@1.0.0 | /data/attributes/dates |
| title | source · DataCite | connector:datacite@1.0.0 | /data/attributes/titles/0/title |
| updated_date | source · DataCite | connector:datacite@1.0.0 |