Effect of Hot Deformation on Microstructure, Hardness and Precipitation Kinetics in a C350 Maraging Steel Modified by Titanium Addition

These properties are obtained by quenching and aging treatments, where the precipitation of intermetallic compounds is promoted in a martensitic matrix. In this context, this paper aims to evaluate the effect of hot deformation on microstructure, kinetics and formation of reverted austenite in a C350 maraging steel modified by titanium addition, in order to improve the mechanical properties without addition of alloying elements.

The following characterization techniques were used: optical microscopy (OM), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM), X-Ray Diffraction (XRD), Vickers microhardness and Dilatometry. The results showed that the deformation promoted a refinement of martensitic packages and blocks, proportional to the reduction of height and a preferred alignment towards the center of the sample. In the aging treatment, the deformation accelerated the kinetics of precipitation and formation of reverted austenite.