Corrosion Behavior of Plasma Nitrided and Nitrocarburised Supermartensitic Stainless Steel

In the present study, SMSS specimens (UNS S41425) were solution heat treated and air cooled followed by plasma nitriding and nitrocarburising at 400, 450 and 500°C for 5h. The produced layers were characterized by optical microscopy, microhardness testing, X-ray diffraction and corrosion testing in NaCl 3.5% solution.

Surface alloying with nitrogen or both nitrogen and carbon results in increased surface hardness and homogeneous layers in which layer thickness increases with temperature. However, plasma nitriding yields a slightly thicker case than nitrocarburising. X-ray diffraction indicates very broad and overlapped peaks for the treatments conducted at 400°C. Increasing treatment temperature appears to result in the formation of chromium nitrides and iron nitrides and carbides, depending on the treatment.