Thermal stability study of Pd-composite membrane fabricated by surfactant induced electroless plating (SIEP)

In this study, Pd composite membranes on macroporous stainless steel substrate (MPSS) were fabricated using CEP and novel surfactant induced electroless plating (SIEP) methods. The structural characteristics of CEP and SIEP fabricated Pd membranes were investigated before and after the heat treatment using SEM, XRD, EDS, and AFM techniques.

The H 2 permselectivity performance of the SIEP membranes was compared with that of CEP at different temperatures and trans-membrane pressures in the range of 523-823 K and 20-100 psi, respectively. The long-term thermal stability test of SIEP fabricated membranes was carried out on two different membranes, fabricated on MPSS substrates with and without oxide layer at 15 psi trans-membrane pressure and thermal cycling of 573-723-573 K. The microstructure analysis revealed that SIEP membranes have finer grains and diffused grain boundaries resulting in uniform, smooth, continuous, and pinhole free Pd-film.