Development of n+np+ solar cells in 100 µm thick silicon wafers

To lower the costs, the reduction of the current wafer thickness from 180-200 µm to 100-120 µm has been proposed. Although the p-type silicon is used to manufacture solar cells, it is susceptible to degradation due to boron-oxygen interaction.

The devices manufactured in n-type silicon wafers doped with phosphorus do not present such degradation and has the potential of achieving higher efficiencies due to the larger minority charge carrier lifetime. The aim of this work is to present the development of n+np+ solar cells fabricated in Cz silicon wafers 100 μm thick. Thin devices were manufactured with the n+np+ structure and compared to n+pp+ devices manufactured in standard thick wafers.