Structure · dataset · 2017
Analyzing the compressive behavior of porous Ti6Al4V by X-ray microtomography
Listed in DataCite
Samples with 40% vol. of pores and a pore size distribution between 100 and 500 µm were produced by powder metallurgy from Ti6Al4V alloy powders.
Description
Sintering was performed at 1300 °C during one hour in an inert Argon atmosphere in a vertical dilatometer. The compressive strength and the porosity of these samples was investigated before and after compression tests through X-ray microtomography.
The values of the elastic modulus (8GPa) and yield strength (80MPa) are within the range of those used in bone implants. Porosity leads to greater deformation whereas fracture of compacts occurs perpendicularly to the applied load. It was determined that the origin of the failure is generated by rupture of interparticle necks and, large pores enhance the propagation of cracks.
Links
Where it is published
- Repository landing page scielo.figshare.com/articles/Analyzing_the_compressive_behavior_of_porous_Ti6Al4V_… ↗
landing page · from DataCite
- DOI doi.org/10.6084/m9.figshare.5666722.v1 ↗
DOI / persistent id · from DataCite
Documentation and papers
- Creative Commons Attribution 4.0 International creativecommons.org/licenses/by/4.0/legalcode ↗
license · from DataCite
- IsSupplementTo 10.1590/1980-5373-mr-2017-0510 doi.org/10.1590/1980-5373-mr-2017-0510 ↗
publication · from DataCite
Catalogue records · 2
- DataCite API api.datacite.org/dois/10.6084/m9.figshare.5666722.v1 ↗
metadata API · from DataCite
- DataCite Commons commons.datacite.org/doi.org/10.6084/m9.figshare.5666722.v1 ↗
catalogue entry · from DataCite
Topics
- Stated by source
- Chemical engineering · Materials engineering
- Inferred from text
- Resources engineering and extractive metallurgy 75%
Related
Provenance · 1 source records, 11 field assertions
| Source | Key | Last seen | Raw |
|---|---|---|---|
| DataCite | 10.6084/m9.figshare.5666722.v1 | 12 d ago | JSON v1 |
| Field | Assertion | Extractor | Evidence |
|---|---|---|---|
| access_level | source · DataCite | connector:datacite@1.0.0 | /data/attributes/rightsList |
| byte_size | source · DataCite | connector:datacite@1.0.0 | |
| concepts[field].anzsrc:group:4019 | enrichment · DataCite | taxonomy-embedding@1.1.0 | title+keywords+description (75%) |
| concepts[field].fos:chemical-engineering | source · DataCite | connector:datacite@1.0.0 | |
| concepts[field].fos:materials-engineering | source · DataCite | connector:datacite@1.0.0 | |
| created_date | source · DataCite | connector:datacite@1.0.0 | |
| description | source · DataCite | connector:datacite@1.0.0 | /data/attributes/descriptions |
| license | source · DataCite | connector:datacite@1.0.0 | /data/attributes/rightsList |
| publication_date | source · DataCite | connector:datacite@1.0.0 | /data/attributes/dates |
| title | source · DataCite | connector:datacite@1.0.0 | /data/attributes/titles/0/title |
| updated_date | source · DataCite | connector:datacite@1.0.0 |