Hard X-ray nanotomography reveals anomalous and expected thermal coarsening behaviour of nanoporous gold

Ptychographic X-ray computed tomography was used to image nanoporous gold samples, with and without metal oxide additives, following incremental ex situ annealing steps up to 750 °C. Studying the exact same sample volumes following sequential annealing steps allowed accurate 3D imaging of large meso- and macropore systems over extended sample volumes. Extraction of surface area, pore size distribution, and pore connectivity were demonstrated using a skeletonization method.

These properties are relevant in the study of functional materials such as catalysts which rely on diffusion processes within the pores. Samples with metal oxide additives were found to be more resistant to thermal annealing and gold ligament coarsening up to 550 °C, while pure nanoporous gold showed a greater loss of specific surface area during the same treatment. An anomalous stabilisation effect was observed during measurements in ambient air, with minimal coarsening observed in sample regions previously exposed to X-rays, and extensive coarsening in neighbouring regions of the same sample which were not previously exposed to X-rays.