Preparation and Characterizations of Monocrystalline Na Doped NiO Thin Films

The spray pneumatic method was used to deposit the Na doped NiO thin films in the range 0 to 5 wt.%, it are investigated at a substrate temperature of 420 °C with NiO solution 0.1 M. Firstly in the XRD specra, as found that a only (111) peak was observed for Na doped NiO thin film indicate that the Na doped NiO thin films a monocrystalline in nature with cubic structure.

The maximum crystallite size of Na doped NiO thin films was 18.90 nm at 3 wt.%. Secondary, the optical transmissions spectra Na doped NiO thin films having a high transparency with comparing to undoped film in visible region. The band gap energy was decreased after doping by Na and reaching a minimum value is 3.53 eV at 2 wt.%.