The influence of segregation of Mn on the recrystallization behavior of C-Mn steels

A homogenization heat treatment was used to remove Mn segregation, while maintaining a similar initial austenite grain size to the segregated condition, to provide base-line comparison data. Deformation trials were carried out in a Gleeble thermomechanical simulator to 0.3 strains at 900 °C, and significant differences in both recrystallization times and final grain sizes were seen between the two conditions.

The segregated sample incurred a longer recrystallization time and a wider recrystallized grain size distribution than the homogenized sample. A finite element model was used to predict the local deformation strains based on variations in material properties caused by segregation; the model used data from XRF elemental mapping of Mn to define the local mechanical properties based on differences in solid solution strengthening.