Data for Effect of HCl cleaning on InSb–Al2O3 MOS capacitors

X-ray photoelectron spectroscopy measurements indicate that HCl diluted in and rinsed with isopropanol (IPA) results in a surface layer of InCl3 which is not present for similar HCl-water processes. Furthermore, this InCl3 layer desorbs from the surface between 200 °C and 250 °C. Metal–oxide–semiconductor capacitors were fabricated using atomic layer deposition of Al2O3 at 200 °C and 250 °C and the presence of InCl3 was associated with a +0.79 V flatband voltage shift.

The desorption of the InCl3 layer at 250 °C reversed this shift but the increased process temperature resulted in increased interface-trapped charge (D it) and hysteresis voltage (V H ). This shift in flatband voltage, which does not affect other figures of merit, offers a promising route to manipulate the threshold voltage of MOS transistors, allowing enhancement-mode and depletion-mode devices to be fabricated in parallel.<br><br>The XPS data includes VAMAS files that contain the measured XPS data and modelled (fitted) components - one file for the samples treated in the HCl-water solution and a separate file for the sample treated in the HCl-IPA solution.