Investigation on the Wear Properties of Ti/TiC/TiN Composite Coatings Prepared by Powder Cored Wires Through TIG Method at Nitrogen Atmosphere on Titanium Substrate

The TIG procedure was done at same welding parameters for all of prepared samples. Phase analysis and microstructures were done by X-ray Diffraction (XRD), Energy-Dispersive X-ray Spectroscopy (EDS), Optical Microscopy (OM) and Scanning Electron Microscopy (SEM).

The obtained results from XRD and EDS demonstrated that the presence of crystalline phases of TiC, TiN and Ti. SEM and OM exhibited formation of the spherical and dendritic TiC particles in a martensitic matrix and also, TiN pinhole areas with rough and collapsed arms. Maximum microhardness value obtained was 571 HV in the case of sample treated with TiC cored wire at 95%argon+5% nitrogen atmosphere.