Data for Exploiting the flexibility of the pyrochlore composition for acid-resilient Iridium oxide electrocatalysts in proton exchange membranes

The materials crystallise from aqueous solution under alkali hydrothermal conditions with 10-40 nm crystallite size. Refinement of their crystal structures using both powder neutron and X-ray diffraction determined the composition of the materials, and Ir LIII-edge XANES spectroscopy shows the average Ir oxidation state to be close to 4.5 in all materials, consistent with bond valence sums.

All materials show high electrocatalytic activity for the oxygen evolution reaction and the electrocatalyst which best maintains activity on cycling is the sodium-free Ca2-xIr2O6·nH2O, while the (Na,Ca)2-xIr2O6·nH2O material shows highest activity when normalised for surface area. In membrane electrode assemblies, carbon corrosion is minimised, making the materials suitable for use in catalyst layers in proton exchange membrane devices, such as electrolysers and fuel cells.