Effect of thermal treatment on points defects of Al-N codoped ZnO films

ZnO films were deposited by sputtering technique on silicon substrates at 20 ºC, Al-concentration was kept constant and N-flow was changed to 6, 12 and 15 sccm. A thermal treatment was performed by annealing the sample during 30 minutes at 300, 400, 500, 600 and 700 °C. Before annealing, Raman spectra shows two vibration modes located at 275 and 580 cm-1 associated to the nitrogen incorporation and the presence of point defects.

Both Raman intensities of modes I275 and I580 decreases when the nitrogen flow increases from 6 to 12 and 15 sccm, which is originated by a decreasing interstitial defects density. The improving of the crystal quality was confirmed by x-ray diffraction and room temperature photoluminescence measurements. After annealing, in the Raman spectra it was observed that I275 increases as the temperature increase, reaches a maximum intensity between 500 and 600 °C, and decreases for higher temperatures.