Post-Curing as an Effective Means of Ensuring the Long-Term Reliability of PDMS Thin Films for Dielectric Elastomer Applications

In this study, the effect of post-curing was investigated for commercial silicone elastomer thin-films as a means of improving long-term elastomer film reliability. The Young's moduli and electrical breakdown strengths of commercial (silica-reinforced) PDMS elastomer films, with and without additional 35 parts per hundred rubber (phr) titanium dioxide (TiO 2 ), were investigated after high-temperature (200°C) post-curing for various timespans.

The elastomers were found to contain less than 2% of volatiles (significantly higher for TiO 2 -filled samples), but nevertheless a strong effect from post-curing was observed. The young's moduli as well as the strain-dependent behaviour were found to change significantly upon post-curing treatment where Young's moduli at 5% strain increases with post-cure. Furthermore, the determined dielectric breakdown parameters from Weibull analyses showed that greater electrical stability and reliability could be achieved by post-curing the PDMS films before usage, and this method therefore paves a way towards more reliable dielectric elastomers.