Plasmon energy changes in FeMo14C15B6Erx (x=0-2) bulk metallic glass during in-situ heating

The plasmon energy was found to decrease with increasing temperature, due not only to thermal expansion but also to chemical reordering in the glasses. The chemical reordering stimulates a specific solute cluster formation; M23(C, B)6 solute clusters began to form above about 200°C in both ribbon and bulk FeMo14C15B6Erx (x=0, 0.5, 1) metallic glasses.

The formation of the M23(C, B)6 solute clusters was only found above 400°C in the ribbon FeMo14C15B6Er2 metallic glass, indicating inhibition of the M23(C, B)6 solute clusters occurred owing to the formation of Er-(C, B) complexes/clusters. The Er-(C, B) complexes/clusters were formed in the cooling process of the sample fabrication. In contrast to the ribbon sample, the formation of the M23(C, B)6 solute clusters did not occur in the bulk FeMo14C15B6Er2 metallic glass during heating.