Conformal MXene Surface Engineering Enables Ultra-Low-Energy Fiber-Laser Powder Bed Fusion of PEEK Composites

Here, Ti3C2Tx MXene nanosheets were conformally assembled on PEEK particles by electrostatic adsorption to construct Ti3C2Tx-sheathed powders with improved NIR absorption, heat transfer, and flowability.

The modified powders enable stable multilayer fiber-laser powder bed fusion (f-LPBF) at ultralow volume energy densities. For PEEK/M1, the required energy density was reduced from 26.667 to 0.333 Jmm-3, representing a 98.75% reduction relative to pristine PEEK, while maintaining a broader processable window and suppressing carbonization-induced instability. The printed S-PEEK/M1 composites showed enhanced interlayer fusion, smoother surfaces, increased crystallinity, and a transcrystalline microstructure, resulting in a tensile strength of 71.71 ± 5.06 MPa, a flexural strength of 87.35 ± 8.02 MPa, and a Vickers hardness of 39.78 ± 3.22 HV.