Heat Treatment of Sintered Valve Seat Inserts

The VSIs were obtained from three different alloys by mixing iron powder with AISI M3:2, AISI M2 high-speed steels, and AISI D2 tool steel. After sintering, the VSI were quenched in air followed by double tempering at seven different temperatures.

The cooling rate during air quenching was measured by means of a thermocouple type k attached to a data acquisition system. The characterization of the mechanical and physical properties of the VSIs was achieved by measuring relative density, apparent hardness and crush radial strength. The resulting microstructures for the sintered parts were interpreted using the isothermal and continuous cooling transformation diagrams for similar alloys.