Dielectric analysis of polypropylene (PP) and polylactic acid (PLA) blends reinforced with halloysite nanotubes

Permittivity values slightly decreased as the HNT content increased from 0 to 2 wt%. It increased at 4 wt% of HNT and again slightly decreased at 6 wt% of HNT, and with further increase in HNT (HNT 8 and HNT 10) led to increase in permittivity values. Loss factor values decreased slightly as the HNT content in the composites increased from 0 to 4 wt%; but with further increase in HNT, the loss factor showed a sharp increase.

Loss tangent (tan δ ) values decreased up to 4 wt% of HNT (HNT 4) and then increased up to 8 wt% (HNT 8) of HNT and then decreased slightly (for HNT 10). Analysing the different dielectric properties, consistent properties were shown by 6 wt% of HNT similar to static and dynamic mechanical properties. The analysis showed that the composites can be utilized in microelectronic devices or in microelectronic packaging applications.